Influences of pretreatment temperature on the surface silylation of diatomaceous amorphous silica with trimethylchlorosilane
Date
2006-08Author
Yuan, Peng
Yang, Dan
Lin, Zhongyu
林种玉
He, Hongping
Wen, Xiaoyan
Wang, Linjiang
Deng, Feng
Collections
- 化学化工-已发表论文 [14469]
Abstract
Diatomaceous amorphous silica samples were modified by silylation using trimethylehlorosilane (TMCS). The resultant materials were characterized by using thermogravimetry (TG), H-1 magic-angle spinning nuclear magnetic resonance (H-1 MAS NMR), Fourier transform infrared spectroscopy (FTIR) and chemical analysis. The degree of silylation was found to increase with the increasing temperature of thermal pretreatment on diatomaceous silica prior to silylation. Increment of the pretreated temperature leads to stepwise removal of physisorbed water followed by the dehydration of capping water that H-bonded with the surface silanols, resulting in exposure of more and more isolated and H-bonded silanols previously covered by water molecules. Among these exposed silanols, isolated silanols show high activity for silylation reaction but H-bonded ones show poor activity. The maximum degree of surface attachment of TMCS grafted onto the diatomaceous silica (about 1.81 mmol TMCS groups per gram of silica) was shown in the sample pretreated at 1100 degrees C, in which the amount of exposed isolated silanols get the maximum. The fundamental information derived from this work is of significance in well understanding the surface silylation reaction of diatomaceous silica and providing useful information for related industrial production. (c) 2006 Elsevier B.V. All rights reserved.
Citation
JOURNAL OF NON-CRYSTALLINE SOLIDS,2006,352(36):3762-3771URI
http://dx.doi.org/doi:10.1016/j.jnoncrysol.2006.05.035https://dspace.xmu.edu.cn/handle/2288/9945