Silicon Silver Composite Materials for Li-ion Batteries
- 2009年第15卷 
应用机械合金化法制备了两种不同组分的Si-Ag复合材料.扫描电镜(SEM)、X射线衍射(XRD)、充放电测试和循环伏安法对该材料的微观形貌、相组成及电化学性能.研究表明,组成原子比为1∶1的复合材料具有很好的循环稳定性和可逆性,在0.2mA·cm-2的电流密度下,经50周循环后可逆容量仍保持300mAh·g-1.实验发现,借助充放电控制,即可有效提高合金材料的循环性能.Si-Ag composite materials were prepared by mechanical alloying method. The morphology and composition of SiAg composites were investigated by SEM and XRD. The electrochemical properties of the composites were determined by charge-discharge tests and cyclic voltammetry. The composite composed of Si∶Ag with an atomic ratio of 1∶1 (sample 1#) showed good cyclic stability and charge-discharge reversibility. The reversible capacity of the composite (sample 1#) was remained over 300 mAh·g-1 after 50 cycles. Experimental results showed that controlling the potential range of charge-discharge processes could enhance the cyclic performance of alloy materials.