Electrochemical Synthesis of Ferrate(VI) by Anodic Oxidation
- 2004年第10卷 
采用电化学阳极氧化法制备高铁酸盐,研究制备条件对电解产率的影响.结果表明,灰口铸铁是较为理想的阳极材料.在以14mol·dm-3NaOH作电解液、20℃和电流密度4.54mA·cm-2条件下电解1h,得最高电流效率为68.5%,优于使用KOH作电解液.The ferrate(Ⅵ) was synthesized by electrochemical anodic oxidation. The effects of preparation conditions on the current yield of ferrate(VI) synthesis have been studied in this work. The experimental results showed that grey cast iron as an anodic material is suitable for electrochemical synthesis and NaOH solution as an electrolyte results in a higher current yield than KOH solution. The highest current yield was obtained at a current density (4.54) mA· cm~(-2),temperature 20 ℃ and 14 mol·dm~(-3) NaOH. In this case, a current yield of 68.5% was obtained by electrolysis for 1 h.