Studies on the Anti-corrosion Behavior of Corrosion Inhibitor to the Ship Building Steel in Moist Air
ZHAO Yong tao
WU Jian hua
- 2001年第7卷 
模拟 90 7A钢在海水的潮湿大气环境和表面覆有薄层缓蚀剂液膜状态下其腐蚀受抑制的情况 ,利用恒电量仪连接ACM控头 ,监测其腐蚀状态 ,结合电化学阻抗谱 (EIS)的测量 ,探讨 90 7A钢在薄层缓蚀剂液膜下的腐蚀受到抑制机理 .结果表明 :此时大气腐蚀反应已转变为阳极过程控制占优势 ,在浸润后期的EIS呈现出由腐蚀介质扩散和电化学放电混合控制特征 ,如果利用恒电量激励下的等效电路模型解析 ,则可以更清楚地获知薄层缓蚀剂液膜下金属表面膜层的信息The anti corrosion behavior of 907A steel, which were covered with thin inibitor layers in moist air, were simulated, The electrochemical measurements, including EIS method and the coulostatic method, were used to atmospheric corrosion monitor(ACM)under thin inhibitor layers to study the mechanism of rust preventiion. the results shown that the mechanism of inhibiting corrosion was different from the steel immersed in inhibitor solutin, the anodic reaction process under thin inhibitor layers had the advantage over that of cathodic for blocking the speed of corrosion. At the later stage of soaking, the blend feature due to the electrochemical process and the diffuse process, had appeared in the EIS plot. The electrochemical parameters of the film forming under thin inhibitor layers could be got easly by the coulostatic method.