Preparation and Visible Light Photocatalytic Activity of Fe-N Codoped TiO2 Nanotube Arrays
- 化学化工－已发表论文 
[中文文摘]应用电化学阳极氧化法结合浸渍和退火后处理制备了Fe和N共掺杂的TiO2纳米管阵列光催化剂,并用场发射扫描电镜(FESEM)、X射线衍射(XRD)、X射线光电子能谱(XPS)和俄歇电子能谱(AES)仪对其进行了表征.结果表明,Fe、N共掺杂对TiO2纳米管阵列的形貌和结构没有明显影响,Fe和N均掺入了TiO2晶格.紫外-可见(UV-Vis)漫反射光谱显示Fe和N共掺杂TiO2纳米管阵列的吸收带边较纯TiO2纳米管阵列和单一掺杂TiO2纳米管阵列红移,可见光吸收增强.以可见光催化降解罗丹明B(RhB)考察了材料的光催化活性,Fe和N共掺杂TiO2纳米管阵列对RhB的降解速率较纯TiO2纳米管阵列和单一掺杂TiO2纳米管阵列明显提高,证明了Fe、N共掺杂产生的协同效应提高了TiO2纳米管阵列在可见光照射下的光催化活性. [英文文摘]Fe-N codoped TiO2 nanotube arrays were fabricated by anodization of Ti, followed by wet immersion and annealing post-treatment. The doped TiO2 nanotube array photocatalysts were characterized by field-emission scanning electron microscopy (FESEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), and Auger electron spectroscopy (AES). The results indicated that Fe and N dopants had almost no effect on the morphology and structure of TiO2 nanotube arrays, and that Fe and N were doped into the TiO2 lattice. UV-Vis diffuse reflectance spectra showed that the absorption band edge of Fe-N codoped TiO2 nanotube arrays exhibited a red shift compared with that of pure TiO2 nanotube arrays and Fe- or N-doped TiO2 nanotube arrays. The photocatalytic activity of Fe-N codoped TiO2 nanotube arrays was evaluated by their ability to degrade rhodamine B under visible light irradiation. The degradation rate of rhodamine B over Fe-N codoped TiO2 nanotube arrays was obviously higher than that over pure TiO2 nanotube arrays and Fe- or N-doped TiO2 nanotube arrays, which is attributed to the synergistic effect of the Fe and N codopants.