Electrochemical impedance spectroscopic study of the first delithiation of spinel lithium manganese oxide
- 化学化工－已发表论文 
The first delithiation of the spinel LiMn2O4 electrode was studied using electrochemical impedance spectroscopy (EIS). Appropriate equivalent circuits were proposed to fit the experimental EIS data. Based on the fitting results, the variation of the capacitance and the resistance of SEI (solid electrolyte interphase) film, the resistance of charge transfer, and the capacitance of double layer along with the increase of polarization potential were quantitatively analyzed. The results demonstrated that the resistance and the thickness of the SEI film formed on the spinel LiMn2O4 electrode were both increased with the increase of polarization potential in the first delithiation of the spinel LiMn2O4 electrode; The charge transfer resistance decreases below 4.15 V and increases above 4.15 V, corresponding to the two-step reversible (de)intercalation of lithium between LiMn2O4 and lambda-MnO2; The double layer capacitance was influenced by both the state of the spinel LiMn2O4 electrode (different polarization potential) and the two-step reversible (de)intercalation of lithium.